湍流腐蚀,turbulent flow corrosion
1)turbulent flow corrosion湍流腐蚀
1.The test and analysis conclude that the cracking failure of minimum flow by-pass line of high-pressure lean amine pump in the hydrocracker are caused by sulfur stress corrosion andturbulent flow corrosion, which are aggravated by pipeline vibration.经过检测分析认为加氢裂化装置高压贫胺液泵最小流量控制阀副线的腐蚀开裂原因是胺液和硫 化氢的应力腐蚀和湍流腐蚀,管线振动加剧了腐蚀。
2)turbulence and erosion corrosion湍流腐蚀和冲蚀
1.The result indicates that electrochemical corrosion,pitting,turbulence and erosion corrosion and their interaction are the main causes of the perforating and leaking of the tubes.结果表明,空冷器管束在失效环境中发生了腐蚀减薄和穿孔泄漏的主要原因是电化学腐蚀、坑蚀、湍流腐蚀和冲蚀以及他们的交互作用引起的。
3)corrosion current腐蚀电流
1.The electrochemical polarization results proved that the spreading rate of micro-droplets increased linearly with the polarization current,and thecorrosion current established by the potential differen.电化学极化结果显示,微液滴的成核速率随极化电流的增加而线性加速,促使大气腐蚀过程发生的电位差和相应的腐蚀电流是微液滴形成和发展的推动力。
2.Based on the results of electrochemical polarization,thecorrosion current of a.电化学极化结果显示,大气腐蚀过程中的腐蚀电流是微液滴形成和发展的推动力。
3.5 and QAl 10-4-4 in NaCl solution,and theircorrosion currents during coupling with bronze alloy QAl 9-2 were measured by electrochemical methods.应用电化学测试手段 ,针对 2 0、2Cr13、QAl 9-2、QAl 10 -3 -1 5和QAl 10 -4-4五种材料试件 ,分别测定了它们在NaCl溶液中的腐蚀电位及与QAl 9-2偶接时的电偶腐蚀电流的变化 。
英文短句/例句
1.DISTRIBUTION OF CORROSION POTENTIAL AND CORROSION CURRENT OF REBARS IN CONCRETE STRUCTURE NEARBY LIQUID LEVEL混凝土结构中钢筋腐蚀电位与腐蚀电流在液面附近的分布
2.corrosion prevention by galvanic polarization电流极化抗腐蚀处理
3.The Stray Current Corrosion Research on the Ship Berthing at the Steel Sheet Dock;钢板桩码头靠泊船杂散电流腐蚀研究
4.Status in Research on Stray-current Corrosion of Buried Steel Pipelines埋地钢质管道杂散电流腐蚀研究现状
5.Electrochemical Corrosion Behavior of Pure Iron in Flowing Seawater纯铁在流动海水中的电化学腐蚀行为
6.Design and Application of Discharge Technique for Control of Stray Current Corrosion to Electric Pumps at Oil Wells of Daqing Oil Fields油田电泵井套管杂散电流腐蚀排流设计及应用
7.Corrosion Effects and Evaluation Method of UHV Power Line Tower Grounding Collection Caused by DC Current特高压直流入地电流对附近杆塔地网腐蚀评估
8.Study and Test of Electrolytic Corrosion for HVDC Support Insulator高压直流支柱绝缘子电化学腐蚀试验研究
9.Study on AC Etching of Aluminium Foil Used in Capacitor under Effect of Additives;添加剂作用下电容器用铝箔交流腐蚀研究
10.Research on preventing corrosion of electric tower caused by grounding current of DC electrode接地极入地电流对杆塔腐蚀及防护研究
11.Monitoring of corrosion rate of steels in marine atmosphere by hydrogen permeation current investigation氢渗透电流法监测海洋大气中钢材的腐蚀速率
12.Research of Stray Current Corrosion Principle and Prevention Measures for Subway地铁杂散电流腐蚀机理以及防护措施研究
13.EFFECT OF STRAY CURRENT OF URBAN RAIL ON BURIED PIPELINE CORROSION城市轨道交通杂散电流对埋地管线腐蚀的影响
14.Corrosion Caused by Stray Current on Mao Ming Section of The Zhan Jiang-Mao Ming Oil Pipeline湛茂输油管道茂名段杂散电流的腐蚀及防腐方法
15.graphite electrode for spark erosion电火花腐蚀用石墨电极
16.electrochemical etching and replating process电化腐蚀和电镀工艺
17.spark erosion machine电火花腐蚀加工机床
18.Are battery connections corroding?电瓶连线是否腐蚀？
相关短句/例句
turbulence and erosion corrosion湍流腐蚀和冲蚀
1.The result indicates that electrochemical corrosion,pitting,turbulence and erosion corrosion and their interaction are the main causes of the perforating and leaking of the tubes.结果表明,空冷器管束在失效环境中发生了腐蚀减薄和穿孔泄漏的主要原因是电化学腐蚀、坑蚀、湍流腐蚀和冲蚀以及他们的交互作用引起的。
3)corrosion current腐蚀电流
1.The electrochemical polarization results proved that the spreading rate of micro-droplets increased linearly with the polarization current,and thecorrosion current established by the potential differen.电化学极化结果显示,微液滴的成核速率随极化电流的增加而线性加速,促使大气腐蚀过程发生的电位差和相应的腐蚀电流是微液滴形成和发展的推动力。
2.Based on the results of electrochemical polarization,thecorrosion current of a.电化学极化结果显示,大气腐蚀过程中的腐蚀电流是微液滴形成和发展的推动力。
3.5 and QAl 10-4-4 in NaCl solution,and theircorrosion currents during coupling with bronze alloy QAl 9-2 were measured by electrochemical methods.应用电化学测试手段 ,针对 2 0、2Cr13、QAl 9-2、QAl 10 -3 -1 5和QAl 10 -4-4五种材料试件 ,分别测定了它们在NaCl溶液中的腐蚀电位及与QAl 9-2偶接时的电偶腐蚀电流的变化 。
4)flow corrosion流动腐蚀
1.The analysis offlow corrosion exhibits that flow velocity,flow state,angle of attack as well as properties of solid particles in solid- liquid flow are the main factors forflow corrosion.流动腐蚀是引起腐蚀破坏的重要原因。
5)AC etching交流腐蚀
1.Study onAC etching process of aluminum capacitor foil for low voltage applications;低压铝箔交流腐蚀工艺研究
6)flow-induced corrosion流动腐蚀
1.Finally theflow-induced corrosion rate of metal electrode was increased by the synergism effect.随着流速增大,电极表面受到的切应力增大,反应阻抗减小,电化学腐蚀加速,协同效应增强,结果使电极流动腐蚀速度增加。
2.The complexity offlow-induced corrosion was described and all kinds of corrosion pattens in flowing media were classified.阐述了流动腐蚀的复杂性与分类 。
3.5% NaCl solution is set up on the basis of determining main controlling factors and their degree of influence inflow-induced corrosion by some electrochemical experiment.针对管流体系 ,根据动量、能量和质量守恒原理 ,应用壁函数、k -ε湍流运动模型确立了管流体系中的计算流体力学模型和质量传递模型 ;结合腐蚀实验确定双相不锈钢流动腐蚀过程中的主要控制因素及其影响程度 ,分析了动力学过程 ,建立了双相不锈钢在 3。
延伸阅读
点腐蚀和缝隙腐蚀金属材料接触某些溶液，表面上产生点状局部腐蚀，蚀孔随时间的延续不断地加深，甚至穿孔，称为点腐蚀（点蚀），也称孔蚀。通常点蚀的蚀孔很小，直径比深度小得多。蚀孔的最大深度与平均腐蚀深度的比值称为点蚀系数。此值越大，点蚀越严重。一般蚀孔常被腐蚀产物覆盖，不易发现，因此往往由于腐蚀穿孔，造成突然性事故（见金属腐蚀）。缝隙腐蚀是两个连接物之间的缝隙处发生的腐蚀，金属和金属间的连接（如铆接、螺栓连接）缝隙、金属和非金属间的连接缝隙，以及金属表面上的沉积物和金属表面之间构成的缝隙，都会出现这种局部腐蚀。许多金属材料都能产生点蚀和缝隙腐蚀。不锈钢、铝合金等靠钝化来增强耐蚀性的金属材料，也易产生点蚀和缝隙腐蚀。许多环境介质都能引起金属材料的点蚀和缝隙腐蚀，尤其是含氯离子的溶液。点腐蚀金属表面的电化学不均匀性是导致点蚀的重要原因。金属材料的表面或钝化膜等保护层中常显露出某些缺陷或薄弱点(如夹杂物、晶界、位错等处)，这些地方容易形成点蚀核心。金属浸入含有某些活化阴离子（特别是氯离子）的溶液中，只要腐蚀电位达到或超过点蚀电位（或称击穿电位），就能产生点蚀。这是由于钝化膜在溶液中处于溶解以及可再度形成的动平衡状态,而溶液中的活化阴离子(氯离子)会破坏这种平衡,导致金属的局部表面形成微小蚀点，并发展为点蚀源。例如不锈钢表面的硫化物夹杂的溶解，暴露出钢的新鲜表面，就会形成点蚀源。点蚀的发展是一个在闭塞区内的自催化过程。在有一定闭塞性的蚀孔内,溶解的金属离子浓度大大增加,为保持电荷平衡，氯离子不断迁入蚀孔，导致氯离子富集。高浓度的金属氯化物水解，产生氢离子，由此造成蚀孔内的强酸性环境，又会进一步加速蚀孔内金属的溶解和溶液氯离子浓度的增高和酸化。蚀孔内壁处于活化状态（构成腐蚀原电池的阳极），而蚀孔外的金属表面仍呈钝态（构成阴极），由此形成了小阳极/大阴极的活化-钝化电池体系，使点蚀急速发展。缝隙腐蚀是由缝隙内外介质间物质移动困难所引起的。为此，缝隙的宽度应足够狭小。它的发展也是一个闭塞区内的自催化过程。例如处在海水等介质中的钢制零部件，在缝隙腐蚀的起始阶段，缝隙内外的金属表面都发生以氧还原作为阴极反应的腐蚀过程。由于缝隙内的溶氧很快被消耗掉，而靠扩散补充又十分困难，缝隙内氧还原的阴极反应逐渐停止，缝隙内外建立了氧浓差电池。缝隙外大面积上进行的氧还原阴极反应，则促进缝隙内金属阳极溶解。缝隙内金属溶解产生过剩的金属阳离子(Me+),又使缝隙外的氯离子迁入缝隙内以保持电平衡。随之而发生的金属离子水解，使缝隙内酸度增高，又加速了金属的阳极溶解（见图)。点腐蚀和缝隙腐蚀的比较点腐蚀和缝隙腐蚀两者的发展阶段的机理是一致的，但是它们的诱发机理和发生过程则有所不同。前者是由于材料的钝态或保护层的局部破坏所引起,通过形成点蚀源而发展起来的;后者则是因介质的电化学不均匀性所引起，腐蚀一开始就在缝隙条件下受闭塞电池的作用。从电极电位来看，发生和发展缝隙腐蚀的电极电位比点蚀更低。从介质来看，缝隙腐蚀在不含氯离子的溶液中也会发生，而点蚀则多在含有特殊的活性阴离子条件下才会发生。溶液中的氯离子浓度对两种腐蚀有很大的影响，通常是氯离子浓度愈高，点蚀和缝隙腐蚀发生的可能性也愈大，而且发展的速度也愈快。其他卤族离子也有类似的影响。一般溶液的温度愈高，产生点蚀和缝隙腐蚀的危险性也愈大。防止措施提高材料耐点蚀性的重要措施是添加适当的合金元素（如在不锈钢中添加钼），采取钝化处理及适当的热处理，降低金属材料中的夹杂物含量。防止缝隙腐蚀的主要措施是在结构中要避免缝隙和能造成表面沉积的几何形状，要尽量用焊接代替铆接，采用非吸湿性材料做垫圈。电化学保护对防止点蚀和缝隙腐蚀都有效。采用合适的耐点蚀和耐缝隙腐蚀的金属材料也是防止点蚀与缝隙腐蚀的有效措施。参考书目Localized Corrosion, National Association of Corrosion Engineers,Houston,Texas,1974.